Table of Contents

## What is the density of 6063 aluminum?

2.70 g/cc

Physical Properties of 6063 Aluminum

Property | 6063-T5 | 6063-T6 |
---|---|---|

Density | 2.70 g/cc | 0.0975 lb/in³ | 2.70 g/cc | 0.0975 lb/in³ |

**How strong is 6063-T6 aluminum?**

6063-T6. T6 temper 6063 has an ultimate tensile strength of at least 190 MPa (28,000 psi) and yield strength of at least 160 MPa (23,000 psi). In thicknesses of 3.15 millimetres (0.124 in) or less, it has elongation of 8% or more; in thicker sections, it has elongation of 10%.

### What is the difference between 6061 T6 and 6063-T6?

Differences Between AL 6061 and AL 6063 6061 aluminum has a lower melting temperature, lower thermal conductivity, and lower heat capacity. AL 6061-T6 has a higher yield strength and fatigue strength when compared to AL-T6 6063. It is also less corrosion resistant than AL 6063.

**What is the difference between 6063-T5 and 6063-T6?**

T5 is a high-temperature forming + artificial aging. It is cooled by a high-temperature molding process and then subjected to a plastic aging state. T6 is solution heat treatment + artificial aging. After the solution heat treatment, the state of artificial aging is performed.

## What is the density of Aluminium alloy?

The density of aluminium is about 2,710kg/m3. The density of the alloys of aluminium does not vary widely from this figure ranging between 2,640kg/m3 and 2,810kg/m3.

**How strong is 6063?**

Mechanical Properties of 6061 Aluminum Versus 6063 Aluminum

6061 | 6063 | |
---|---|---|

Tensile strength | 124-290 MPa | 145–186 MPa |

Yield strength | 276 MPa/40000 psi | 214 MPa/31000 psi |

Fatigue strength | 96.5 MPa/14000 psi | 68.9 MPa/10000 psi |

Hardness (Brinell) | 95 | 73 |

### How do you find the density of aluminium?

Furthermore, for calculating density we divide the mass of the object with its volume (D = m / v). Moreover, the standard unit that we use to measure the density is kilograms per cubic meter (kg/m^{3}).